ZIRCONIA

ZOLID FX WHITE

amann girrbach zolid white

SUPER HIGH TRANSLUCENT ZIRCONIA (SHT)

Zolid FX White, these are super high translucent zirconia blanks used for monolithic or anatomically reduced anterior restorations and up to 3-unit bridges in the molar region. The high-performance ceramic combines the outstanding processing characteristics of zirconia with comparable translucency previously only known in lithium disilicate. The result is highly esthetic restorations with permanent strength and stability. Restorations are processed and fitted intraorally without additional cost using commercially available luting material.


TECHNICAL DATA

Bending Strength: 700 +/- 150 MPa
Modulus of Elasticity: ≥ 200 GPa
Vickers Hardness: 1300 +/- 200 HV10
CTE 25 - 500 °C: 10.1 +-/ 0.5 10–6/K
Chemical Solubility: < 100 μg/cm2
Diameter: 98.5mm
Thickness: 12, 14, 16, 18, 20mm

ZOLID FX MULTILAYER

amann girrbach zolid multilayer

POLYCHROMATIC, SUPER HIGH TRANSLUCENT ZIRCONIA

Zolid FX Multilayer is a polychromatic, super high translucent zirconia with integrated shade and translucency gradient. Smooth shade transitions simulate tooth enamel, dentine and cervical shades in a naturally fluent progression without disruptive shade edges. The tooth-like preshading allows efficient, economical processing without the staining procedure.


TECHNICAL DATA

Bending Strength: 700 +/- 150 MPa
Modulus of Elasticity: ≥ 200 GPa
Vickers Hardness: 1300 +/- 200 HV10
CTE 25 - 500 °C: 10.1 +-/ 0.5 10–6/K
Chemical Solubility: < 100 μg/cm2
Diameter: 98.5mm
Thickness: 14, 16, 20mm

ZOLID HT+ WHITE

amann girrbach zolid ht+ white

HIGHLY TRANSLUCENT ZIRCONIUM OXIDE

Zolid HT+ is a highly translucent zirconium oxide which combines high mechanical characteristics with outstanding esthetics. At over 1000 MPa, its strength lies in the range of the proven Zolid HT zirconium oxide, however, the light-optical properties surpass those of the predecessor considerably. Even large, implant-supported structures with a gingival component radiate the vitality of natural tooth substance due to their high light permeability. Optimised milling processing results in even more delicate margin design, offering exceptional edge stability at the same time. The combination with the Ceramill Liquid "new formula“ staining solutions allows highly esthetic colour shade results corresponding to the VITA classical shade guide.


TECHNICAL DATA

Bending Strength: 1100 +/- 150 MPa
Modulus of Elasticity: ≥ 200 GPa
Vickers Hardness: 1300 +/- 200 HV10
CTE 25 - 500 °C: 10.4 +/- 0.5
Chemical Solubility: < 100 μg/cm2
Diameter: 98.5mm
Thickness: 10, 12, 14, 16, 20, 25mm

ZOLID HT+ PRESHADE

amann girrbach zolid ht+

HIGHLY TRANSLUCENT, PRE-STAINED ZIRCONIUM OXIDE

The highly translucent, monochrome zirconium oxide blanks combine high mechanical indices with excellent aesthetics and the efficiency of pre-stained materials. The significantly increased translu-cency, when compared with its predecessor Ceramill Zolid, also provides massive constructions with natural beautiful and vital aesthetics. Available in 16 A-D shades, Zolid HT+ Preshades offer the highest level of colour reliability and assure reproducible results. By using the Ceramill Stain & Glaze stains and glazing materials, all the VITA Classic tooth shades can even be achieved with a smaller selection of blanks. This leads to customised solutions which fully meet the demands of patients and laboratories.


TECHNICAL DATA

Bending Strength: 1000 +/- 150 MPa
Modulus of Elasticity: ≥ 200 GPa
Vickers Hardness: 1300 +/- 200 HV10
CTE 25 - 500 °C: 10.4 +/- 0.5
Chemical Solubility: < 100 μg/cm2
Diameter: 98.5mm
Thickness: 14, 16, 20mm

ZOLID GEN-X

amann girrbach zolid gen-x

POLYCHROMATIC, HIGHLY TRANSLUCENT ZIRCONIA

Zolid Gen-X puts an end to the time-consuming search for the right blank for the popular restoration, quite simply because the latest blanks of the Zolid DNA generation are true all-rounders!

Zolid Gen-X combines all the advantages of the Zolid HT+ product group: the excellent esthetic properties and outstanding mechanical values allow exceeding any indication limitations.

In addition, Gen-X possesses a natural color gradient that takes the blank to a new level in terms of efficiency and esthetics.


TECHNICAL DATA

Bending Strength: 1000 +/- 150 MPa
Modulus of Elasticity: ≥ 200 GPa
Vickers Hardness: 1300 +/- 200 HV10
CTE 25 - 500 °C: 10.5 +/- 0.5
Chemical Solubility: < 100 μg/cm2
Diameter: 98.5mm
Thickness: 14, 16, 20, 25mm

ZOLID DRS

amann girrbach zolid drs

POLYCHROMATIC, HIGHLY TRANSLUCENT ZIRCONIA (HT+)

Together with the High-Speed Therm DRS sintering furnace, Zolid DRS forms the basis for the High-Speed Zirconia Kit and thus for the ultra-fast fabrication of zirconia restorations. The restorations can be sintered in just 20 minutes and offer maximum efficiency with a natural appearance due to the perfectly coordinated 16 Vita shades with integrated shade and translucency gradient. Numerous studies have confirmed that the fast sintering cycle has no relevant influence on optical or mechanical properties. Both laboratories and dental practices benefit from this innovative High-Speed sintering process enabling them to add the so-called "Same Day Crown" to their service offering. Due to the extremely shortened sintering process, single-tooth crowns and three-pontic bridges can be realized in just one day, from preparation to final insertion.


TECHNICAL DATA

Bending Strength: 1100 +/- 150 MPa
Modulus of Elasticity: ≥ 200 GPa
Vickers Hardness: 1300 +/- 200 HV10
CTE 25 - 500 °C: 10.5 +/- 0,5 x 10–6 K-1
Chemical Solubility: < 100 μg/cm2